1 / 4
Model No. : | 1.2379/SKD11/D2/Cr12Mo1V1 |
---|---|
Brand Name : | Ruisheng |
Product description
C | Si | Mn | Cr | Mo | V | P | S | Co |
1.40-1.60 | 0.10-0.50 | 0.30-0.50 | 11.00-13.00 | 0.70-1.20 | (0.80) | ≤0.025 | ≤0.025 | (0.60) |
Critical point | Ac1 | Acm | Arcm | Ar1 | Ms |
Temperature(Approximation)/°c | 810 | 875 | 750 | 695 | 190 |
Temperature/°c | 20~100 | 20 ~200 | 20~300 | 20~400 |
Coefficient of expansion/°c-1 | 10.5*10-6 | 11.5*10-6 | 11.9*10-6 | 12.2*10-6 |
Item | Heating temperature/°C | start forging temperature/°C | final forging temperature/°C |
cooling |
Steel ingot | 1120-1160 | 1050-1090 | ≥850 | High-temperature annealing |
Steel billet |
1120-1140 |
1050-1070 |
≥ 850 | High-temperature annealing ,pit cold or Sand cold |
Quenching temperature/°c | 900 | 950 | 980 | 1000 | 1030 | 1050 | 1080 | 1100 | 1130 |
Hardness HRC | 52.5 | 57.5 | 60 | 63.5 | 64 | 63 | 62.5 | 62 | 60 |
residual austenite(%) | ---- | 4 | 4 | 4.5 | 6 | 10 | 13 | 24 | ---- |
steel name | after annealed or cold drawn hardness≤HBW | Preheat temperature/°C | Quenching temperature /°C | thermal insulation /min | Cooling medium | Tempering temperature | after tempering hardness≥HBC | ||
annealed | cold drawn | Salt bath furnace | Controlled atmosphere furnace | ||||||
D2 Cr12Mo1V1 | 255 | 269 | 816 | 996 | 1010 |
10-20 | air cooling | 204 | 59 |