Submerged Arc Welding Wires (H08MnA / AWS EM12)

Confirm with:
GB/T 5293 F4A2-H08MnA
AWS A5.17 F6A0-EM12
BS EN 756-S 35 2 FB S2
ISO 14171-A-S 35 2 FB S2
ISO 14171-B-S43A2 FB SU22

KH-H08MnA is a submerged arc welding wire of coppersurfaced carbon structural steel, Be used together with fused flux KJ101. KJ301 is fluorine-alkali agglomerated flux, alkalinity is approx 1.8, It appears a ball granule about 10~60 mesh in size. They are used together, the arc is stable, slag is easy to remove and bead appearance is excellent. The welds has higher low temperature impact resistance.

Model No.: KH-H08MnA
Flux contanining: Containing flux
Diameter: ø 3.2mm, ø 4.0mm
Type: Rolling wire
Weight: 25kg, 50kg, etc.
Export Markets: Gloal

Application:
Suitable for carbon-steeland low alloy steel(16Mn, 16MnCu etc. ).

NOTICE:
1. Dry the flux at 300~350° C for 1~2 hours before, completely remove rust, oil and dirt from the groove surface prior to welding.
2. Before welding, rust, water and impurities are to be removed from the welded surfaces of workplaces.